文獻(xiàn)名： Interaction of hairy carboxyalkyl cellulose nanocrystals with cationic surfactant: Effect of carbon spacer

作者：Zahra Hosseinpour Feizi,Pedram Fatehi 

Biorefining Research Institute, Green Processes Research Centre and Chemical Engineering Department, Lakehead University, 955 Oliver Road, Thunder Bay, ON, P7B5E1, Canada

摘要：Tuning the surface chemistry of nanocellulose is essential for developing its end-use applications. Herein, different carboxyalkylated cellulose nanocrystals (CNC) with similar charge densities but with tunable hairy structures were produced. The effect of carbon spacer of the grafted groups on the interaction of the CNC and a cationic surfactant, myristyl trimethyl ammonium bromide (MTAB), at different pH and salinity was explored. The CNC with longer grafted chain length was more hydrophobic, adsorbed more MTAB, and formed a more compact MTAB adlayer than did CNC with the shorter chain length. Also, the adsorption was higher at neutral pH, implying a high electrostatic attraction and hydrophobic interaction between substrates. The hydrophobic interaction of MTAB and hairy CNC in saline systems improved its adsorption. Although MTAB adsorbed more when its concentration was higher than its critical micelle concentration (CMC), the adsorbed adlayer had a less compact structure on the CNC surfaces.

關(guān)鍵詞：Carboxyalkylation; Carboxybutylation; Carboxyheptanation; Carboxypantadecanation; Cellulose nanocrystals; Cationic surfactant