文獻名： Interaction of Carboxyalkylated Cellulose Nanocrystals and Antibiotics

作者： Zahra Hosseinpour Feizi and Pedram Fatehi

Green Processes Research Centre and Chemical Engineering Department, Lakehead University, 955 Oliver Road, Thunder Bay, Ontario P7B 5E1, Canada

摘要：Although antibiotics are beneficial for treating infections, their release into the environment has raised global concerns. In this work, the interactions of cellulose nanocrystal (CNC) derivatives with sulfamethoxazole (SMX), ciprofloxacin (CIP), and doxycycline (DOX) antibiotics were studied fundamentally. CNC was carboxyalkylated to bear different carbon chain lengths but similar negative charges on its surface. The highest level of adsorption of DOX on the carboxypantadecanated CNC (i.e., carboxyalkylated CNC with more carbon spacer, PCNC) occurred at pH 6.0, which was due to the electrostatic and π interactions along with hydrogen bonding. The contact angle and quartz crystal microbalance (QCM) adsorption analyses revealed a faster interaction and adsorption of DOX than other antibiotics on PCNC. The results also depicted the diffusion of DOX into the porous structure of CNC derivatives, especially that of PCNC. Also, a more compact adsorbed layer of DOX was formed on PCNC than on other CNC derivatives. Carboxyalkylation was observed to slightly reduce the surface area of CNC, while the antibiotic adsorption drastically increased the surface area of CNC due to their adsorption on the surface. XPS analysis revealed that carboxyalkylation significantly enhanced the C–C/C–H bond, while antibiotic adsorption on PCNC enhanced C–N/C–O and C–C/C–H bonds in antibiotic-loaded CNC samples. Overall, carboxyalkylated CNC was observed to have an outstanding affinity for capturing antibiotics, especially DOX, which could pave the way for the use of CNC in such applications that surface/antibiotic interactions were essential.

關鍵詞：carboxyalkylation; adsorption; cellulose nanocrystals; antibiotics; QCM