荷貝克HOPPECKE蓄電池SB12V110規格及參數

荷貝克HOPPECKE蓄電池SB12V110規格及參數

我們的power. XC以緊湊的形式代表創新的AGM設計（網格板和羊毛分離器）。它通過后把手進行了優化運輸。其特殊的網格板設計確保了最大的能量密度。

Wartungsfreiheit hinsichtlichdesNachfüllensvonWasser - durch創新的Gel-ESS Technologie

SehrguteHochstromf?higkeit - geringe Investitionskosten durch innovation Elektrodenstruktur

Optimale Raumausnutzung - durch horizontale Anordnung und Stapelbarkeit

Erh?hteKurzschlusssicherheitschon bei der Montage - durch Verwendung von HOPPECKE System-Verbindern

Einfache Montage und Einbau - Batteriedeckel mit integriertem Griffsystem

Inhalation Sulfuric Acid: Remove to fresh air immediately. Consult a physician. Lead: Remove from exposure, gargle, wash nose and lips; consult physician. Ingestion Sulfuric Acid: Give large quantities of water. Consult a physician. Lead: Consult physician immediately. Skin Sulfuric Acid: Flush with large amounts of water for at least 15 minutes; remove contaminated clothing completely. If symptoms persist, seek medical attention. Wash contaminated clothing before reuse. Discard contaminated shoes. Lead: Wash immediately with soap and water. Eyes Sulfuric Acid and Lead: Flush immediately with large amounts of water for least 15 minutes while lifting lids. Seek immediate medical attention.

閃點(采用的方法)：不可燃的可燃極限：*氫氣體滅火劑：ABC級滅火器，限值：Lel=4.1%(氫氣)UEL=74.2% 在牢房里。熱沖擊可能導致電池外殼和/或外殼破裂。在電池充電過程中可能會產生氫氣。特別消防程序：如果有電池 RGE，關閉電源。使用正壓、自給式呼吸器滅火。施加到電解質上的水產生熱量并使其飛濺。耐磨的衣服。VEVE 傾斜區域良好。 不尋常的火災和爆炸危險： 在正常的電池操作或充電時，電池中會產生氫氣和氧氣氣體。 (氫是易燃的，氧是助燃劑。 (燃燒)在電池過度充電時，這些氣體通過通風口進入空氣。為了避免火災或爆炸的危險，請將火花和其他點火源遠離電池。別這么說 金屬物體同時接觸電池的正負端子。通風良好。

Flash Point (Method Used): non flammable Flammable Limits: *Hydrogen Gas Extinguishing Media: Class ABC extinguisher, Limits: LEL = 4.1% (Hydrogen Gas) UEL = 74.2% NOTE: CO2 may be used, but not directly on the cell. The thermal shock may cause cracking of the battery case and/or cases. Hydrogen gas may be generated during battery charging. Special Fire Fighting Procedures: If batteries are on charge, turn off power. Use positive pressure, self-contained breathing apparatus in fighting fire. Water applied to electrolyte generates heat and causes it to splatter. Wear acid resistant clothing. Ventilate area well. Unusual Fire and Explosion Hazards: Hydrogen and oxygen gases are generated in cells during normal battery operation or when on charge. (Hydrogen is flammable and oxygen supports combustion). These gases enter the air through the vent caps during battery overcharging. To avoid risk of fire or explosion, keep sparks and other sources of ignition away from the battery. Do not allow metal objects to simultaneously contact both positive and negative terminal of batteries. Ventilate area well.

　1、UPS浮充充電時，請用充電電壓2.275V/單格（20℃時的設定值），進行定電壓充電或0.002CA以下的電流進行定電流充電。溫度有0C以下或40C以上時，有必要對充電電壓進行修正，以20C為起點每變化一度，單格電壓變化-3mv。
　　
　　2、循環充電時，充電電壓以2.40-2.50V/單格（20℃時的設定值），進行定電壓電壓充電。溫度在5C以下或35℃以上進行充電時，以20℃為起點，每變化一度充電電壓調整-4mv/單格。
　　
　　3、充電初期電流控制在0.25CA以下。
　　
　　4、充電量設為放電量的100-120%，但環境溫度在5C以下時，設為120-130%。
　　
　　5、溫度越低（5C以下）充電結束時間越長，溫度越高（35C以上）越容易發生過充電，所以特別是在循環使用時，在5C～30C內進行充電較好。
　　
　　6、為防止過充電盡量安裝充電計時器，或自動轉換成涓流式充電方式。
　　
　　7、充電時電池溫度要控制在-15C～+40C的范圍內。

　　
　　二、關于放電
　　
　　放電時請將電池溫度控制在-15℃-+50℃的范圍內。
　　
　　連續放電電流請控制在3CA以下（H控制在6ＣA以下）。
　　
　　放電終止電壓依電流的大小而變化，大體如下所述。注意放時，電壓不得低于下述電壓。
　　
　　放電以后請迅速充電。如不小心過放電之后也請立即充電。